Casting self-hardening furan resin is a kind of amber or brown transparent viscous liquid. This series of product is a new type of casting self-hardening adhesive agent belonging to furan type with complete variety. Adopting advanced synthesis process, the product offers advantages such as high intensity, low viscosity, less odor and good humidity resistance etc., and it is suitable for cast of different kinds of cast steel, cast iron and non-ferrous metal casting.
|
|
FFD-103
|
FFD-105
|
FFD-102
|
FFD-104
|
FFD-111
|
FFD-121
|
FFD-131
|
|
Appearance
|
Jacinth transparent liquid
|
Red brown semitransparent liquid
|
Yellow brown viscous liquid
|
|
Density (20℃) g/cm3
|
1.10-1.20
|
1.10-1.20
|
1.10-1.20
|
1.10-1.20
|
1.15-1.25
|
1.15-1.25
|
1.15-1.30
|
|
Viscosity (20℃) mpa.s
|
14-20
|
15-20
|
≤15-20
|
15-20
|
15-20
|
15-80
|
20-600
|
|
PH Value
|
7.0±0.5
|
7.0±0.5
|
7.0±0.5
|
7.0±0.5
|
7.0±0.5
|
7.0±0.5
|
7.0±0.5
|
|
Content of free formaldehyde %
|
≤0.05-01
|
≤0.1-0.2
|
≤0.1-0.5
|
≤0.1
|
≤0.1
|
≤0.2
|
≤0.3
|
|
Nitrogen content %
|
0.5-2.0
|
3.0-4.0
|
0
|
2.5-3.0
|
≤1.8-2.8
|
≤5.0
|
10-12
|
|
Tensile strength within 24 hours
≥ Mpa
(This intensity value is only for reference.)
|
1.5
|
1.5
|
1.2
|
1.5
|
1.5
|
1.0
|
0.8
|
|
Storage duration（Year）
|
1
|
1
|
1
|
1
|
1
|
1
|
0.5
|
|
Scope of application
|
High section iron,
cast steel
,magnesium iron. ...Export product
|
High section iron, Magnesium iron.... Export product
|
Large cast steel,
high alloy steel export product
|
Alloy steel casting export product
|
Generic cast steel /large cast iron export product
|
Generic cast iron/non ferrous metal export product
|
Cast copper, cast aluminum, mold filling…Export product
|
1 Brief introduction
FFD-1 self-hardening furan resin is a kind of casting resin solidified under atmospheric temperature, it is solidified and popped out by adding benzene sulfonic acid or toluene sulfonic acid catalytic agent.
2 Operation guide
1.Proportion of resin and sand
Sand：Resin（containing silicane）：Curing agent=100：（1.2-3.0）：（0.6-1.5）
2. Method of sand mulling
Add curing agent into sand firstly, perform sand mulling 10-30 seconds with high-speed sand muller or perform sand mulling 30-60 seconds with low-speed sand muller. The second step is to add resin and mix it uniformly 30-60 seconds. When sand mulling is finished, molding and its filling shall be prepared immediately. Long time sand mulling and storage is forbidden.
3 Precautions
1 It is forbidden to directly mix resin with curing agent, otherwise accident may be caused due to fast reaction.
2.Long time sand mulling shall be avoided, otherwise its service time is exceeded and the intensity is decreased.
3. Curing agent is a kind of acidic material, its splashing onto skin or apparel shall be avoided. If curing agent splashes onto skin, immediate clean water rinsing shall be applied, and the serious case must be treated in hospital.
4. Do not deposit resin directly under sunshine or near heat source, otherwise its storage duration will be shortened.