Furan resin for FRP
一、Brief introduction
The product was developed by Architecture Institute of Metallurgy Ministry who refer to the similar product of West Germany and passed the technology appraisal of Metallurgy Ministry.
The Furan resin for FRP (anticorrosive) it is high adherence strength, good heat resistant and good anticorrosive in all organic solvents. It is an ideal adhesive because of its acid resistant and alkali resistant to be used on some occasions where can't use epoxy resin,phenolic resin and unsaturated polyester resin.it consists of liquid and furan resin powder two components.(to produce glass fibre reinforced plastic when mixed with the powder of glass fibre reinforced plastic)
The product shows good resistant to most of acid and alkali and can be used under the temperature of about 220℃. The construction is Convenient, have applied extensively in anticorrosive, The products was developed furan series products
二、Technical Index
|
1.Appearance： Red-brown glutinous liquid
|
|
|
Viscosity: 20-150s(spread-4)
|
Density：≥1.18/cm3
|
|
|
|
|
2.Appearance:
|
Gray powder
|
|
Hardening of time
|
（20℃）No more than 14 hours
|
| |
|
|
三、Proportioning
|
Item
|
Furan resin for FRP
|
|
Furan resin FRP gum
|
1
|
|
Furan resin FRP catalyst powder
|
1.0-1.5
|
四、Main Anticorrosive Property
|
Medium
|
Anticorrosive level
|
Medium
|
Anticorrosive level
|
|
5~60% Sulfuric acid
|
good
|
40% sodium hydroxide
|
Good
|
|
37% Hydrochloric acid
|
passable
|
Toluene, formaldehyde
|
good
|
|
50% zinc sulfate
|
good
|
Methanol, ethanol
|
good
|
|
20% Acetic acid
|
good
|
30% Sodium chloride
|
passable
|
|
10% Nitric acid
|
passable
|
40%sulfuric acid and 10% soda lye to supersede
|
passable
|
|
10% Chromic acid
|
passable
|
15% Hydrogen peroxide
|
passable
|
|
75% phosphoric acid
|
good
|
20% ammonium hydroxide
|
good
|
|
50% carbon bisulfide
|
passable
|
Chlorine
|
passable
|
|
ammonia
|
good
|
Dimethoate
|
Passable
|
|
hydrofluoric acid
|
passable
|
water
|
Good
|
五、 Furan resin for FRP main experiment result
|
Tensile strength
|
Mpa
|
＞80
|
|
Compression strength
|
Mpa
|
＞50
|
|
|
|
|
|
Hardening time
|
30℃,h
|
＜24
|
|
The highest use temperature
|
℃
|
＞220
|
|
|
|
|
六、Usage ：
Furan resin for FRP can use building corrosion resistance, impermeable layer, lining brick plate, Corrosion resistant bricks, casting slabs and granite ， furan resin concrete tank, pool, floor, etc. Also can be used for lining anticorrosion equipment metal protection.
七、Usage methods and Check standard :
The product is of appropriate thickness, good mixedness and reliable quality, according with the current technology standard of anticorrosive engineering and specification for construction and acceptance of anticorrosive engineering of buildings GB 50212-2002
1、 Mix the good furan resin for FRP, considering that must be used in 40 minutes to complete, mix every portion furan resin FRP in 2-3 kilograms . first take out the Furan resin FRP catalyst powder,then take out Furan resin gum, After strict calculation, fully mix can be used. When the environment temperature over 30℃, should reduce ratio.
2、 Please do not use other any curing agent to join in the furan resin gum.
3、 Construction began in may try matching before a portion.
八、Safe Storage and Package (stored in the ventilated and dry place)
The period of validity of Furan resin FRP gum is one year(30-250KG/drums),
the period of validity of Furan resin FRP harden powder is one year (25KG/bag).
Hebei Furan International Co.,Ltd.
Shijiazhuang Worldwide Furfural and Furfuryl ALcohol Co.,LTd
Plant add:Notth Industry In Wuji County area, Shijiazhuang City , China
TEL:0086 311 86683938
FAX:0086 311 8668 2938
MSN:furfurals@yahoo.com.cn
WWW. furanss.com or www.furfuryl.com
e-mail: furfurals@163.com
点击给我留言